7020 Aluminum vs. SAE-AISI M52 Steel
7020 aluminum belongs to the aluminum alloys classification, while SAE-AISI M52 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 7020 aluminum and the bottom bar is SAE-AISI M52 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 190 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 26 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 190 to 390 | |
| 710 to 2280 |
Thermal Properties
| Latent Heat of Fusion, J/g | 380 | |
| 260 |
| Melting Completion (Liquidus), °C | 650 | |
| 1510 |
| Melting Onset (Solidus), °C | 610 | |
| 1470 |
| Specific Heat Capacity, J/kg-K | 880 | |
| 460 |
| Thermal Conductivity, W/m-K | 150 | |
| 31 |
| Thermal Expansion, µm/m-K | 23 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 39 | |
| 8.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 12 |
| Density, g/cm3 | 2.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 7.5 |
| Embodied Energy, MJ/kg | 150 | |
| 110 |
| Embodied Water, L/kg | 1150 | |
| 89 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 47 | |
| 24 |
| Strength to Weight: Axial, points | 18 to 37 | |
| 25 to 80 |
| Strength to Weight: Bending, points | 25 to 41 | |
| 22 to 49 |
| Thermal Diffusivity, mm2/s | 59 | |
| 8.4 |
| Thermal Shock Resistance, points | 8.3 to 17 | |
| 21 to 67 |
Alloy Composition
| Aluminum (Al), % | 91.2 to 94.8 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.85 to 1.0 |
| Chromium (Cr), % | 0.1 to 0.35 | |
| 3.5 to 4.3 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 0.4 | |
| 84.4 to 88.9 |
| Magnesium (Mg), % | 1.0 to 1.4 | |
| 0 |
| Manganese (Mn), % | 0.050 to 0.5 | |
| 0.15 to 0.45 |
| Molybdenum (Mo), % | 0 | |
| 4.0 to 4.9 |
| Nickel (Ni), % | 0 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.35 | |
| 0.2 to 0.6 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 |
| Tungsten (W), % | 0 | |
| 0.75 to 1.5 |
| Vanadium (V), % | 0 | |
| 1.7 to 2.3 |
| Zinc (Zn), % | 4.0 to 5.0 | |
| 0 |
| Zirconium (Zr), % | 0.080 to 0.25 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 |