7049 Aluminum vs. AISI 418 Stainless Steel

7049 aluminum belongs to the aluminum alloys classification, while AISI 418 stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 7049 aluminum and the bottom bar is AISI 418 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
330
Elastic (Young's, Tensile) Modulus, GPa 70
200
Elongation at Break, % 6.2 to 7.0
17
Fatigue Strength, MPa 160 to 170
520
Poisson's Ratio 0.32
0.28
Shear Modulus, GPa 27
77
Shear Strength, MPa 300 to 310
680
Tensile Strength: Ultimate (UTS), MPa 510 to 530
1100
Tensile Strength: Yield (Proof), MPa 420 to 450
850

Thermal Properties

Latent Heat of Fusion, J/g 370
270
Maximum Temperature: Mechanical, °C 180
770
Melting Completion (Liquidus), °C 640
1500
Melting Onset (Solidus), °C 480
1460
Specific Heat Capacity, J/kg-K 860
470
Thermal Conductivity, W/m-K 130
25
Thermal Expansion, µm/m-K 23
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 36
2.8
Electrical Conductivity: Equal Weight (Specific), % IACS 110
3.1

Otherwise Unclassified Properties

Base Metal Price, % relative 10
15
Density, g/cm3 3.1
8.0
Embodied Carbon, kg CO2/kg material 8.1
2.9
Embodied Energy, MJ/kg 140
41
Embodied Water, L/kg 1110
110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31 to 34
170
Resilience: Unit (Modulus of Resilience), kJ/m3 1270 to 1440
1830
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 45
24
Strength to Weight: Axial, points 46 to 47
38
Strength to Weight: Bending, points 46 to 47
29
Thermal Diffusivity, mm2/s 51
6.7
Thermal Shock Resistance, points 22 to 23
40

Alloy Composition

Aluminum (Al), % 85.7 to 89.5
0
Carbon (C), % 0
0.15 to 0.2
Chromium (Cr), % 0.1 to 0.22
12 to 14
Copper (Cu), % 1.2 to 1.9
0
Iron (Fe), % 0 to 0.35
78.5 to 83.6
Magnesium (Mg), % 2.0 to 2.9
0
Manganese (Mn), % 0 to 0.2
0 to 0.5
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0
1.8 to 2.2
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.25
0 to 0.5
Sulfur (S), % 0
0 to 0.030
Titanium (Ti), % 0 to 0.1
0
Tungsten (W), % 0
2.5 to 3.5
Zinc (Zn), % 7.2 to 8.2
0
Residuals, % 0 to 0.15
0