7049 Aluminum vs. EN 1.4335 Stainless Steel

7049 aluminum belongs to the aluminum alloys classification, while EN 1.4335 stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 7049 aluminum and the bottom bar is EN 1.4335 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
170
Elastic (Young's, Tensile) Modulus, GPa 70
200
Elongation at Break, % 6.2 to 7.0
45
Fatigue Strength, MPa 160 to 170
210
Poisson's Ratio 0.32
0.27
Shear Modulus, GPa 27
79
Shear Strength, MPa 300 to 310
400
Tensile Strength: Ultimate (UTS), MPa 510 to 530
570
Tensile Strength: Yield (Proof), MPa 420 to 450
230

Thermal Properties

Latent Heat of Fusion, J/g 370
300
Maximum Temperature: Mechanical, °C 180
1100
Melting Completion (Liquidus), °C 640
1410
Melting Onset (Solidus), °C 480
1370
Specific Heat Capacity, J/kg-K 860
480
Thermal Conductivity, W/m-K 130
14
Thermal Expansion, µm/m-K 23
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 36
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 110
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 10
25
Density, g/cm3 3.1
7.9
Embodied Carbon, kg CO2/kg material 8.1
4.4
Embodied Energy, MJ/kg 140
62
Embodied Water, L/kg 1110
190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31 to 34
210
Resilience: Unit (Modulus of Resilience), kJ/m3 1270 to 1440
130
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 45
25
Strength to Weight: Axial, points 46 to 47
20
Strength to Weight: Bending, points 46 to 47
19
Thermal Diffusivity, mm2/s 51
3.7
Thermal Shock Resistance, points 22 to 23
12

Alloy Composition

Aluminum (Al), % 85.7 to 89.5
0
Carbon (C), % 0
0 to 0.020
Chromium (Cr), % 0.1 to 0.22
24 to 26
Copper (Cu), % 1.2 to 1.9
0
Iron (Fe), % 0 to 0.35
49.4 to 56
Magnesium (Mg), % 2.0 to 2.9
0
Manganese (Mn), % 0 to 0.2
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.2
Nickel (Ni), % 0
20 to 22
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.25
0 to 0.25
Sulfur (S), % 0
0 to 0.010
Titanium (Ti), % 0 to 0.1
0
Zinc (Zn), % 7.2 to 8.2
0
Residuals, % 0 to 0.15
0