7049 Aluminum vs. Sintered 6061 Aluminum
Both 7049 aluminum and sintered 6061 aluminum are aluminum alloys. They have 89% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is 7049 aluminum and the bottom bar is sintered 6061 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 68 |
| Elongation at Break, % | 6.2 to 7.0 | |
| 0.5 to 6.0 |
| Fatigue Strength, MPa | 160 to 170 | |
| 32 to 62 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 25 |
| Tensile Strength: Ultimate (UTS), MPa | 510 to 530 | |
| 83 to 210 |
| Tensile Strength: Yield (Proof), MPa | 420 to 450 | |
| 62 to 190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 170 |
| Melting Completion (Liquidus), °C | 640 | |
| 640 |
| Melting Onset (Solidus), °C | 480 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 860 | |
| 900 |
| Thermal Conductivity, W/m-K | 130 | |
| 200 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 36 | |
| 52 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
| 170 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 9.5 |
| Density, g/cm3 | 3.1 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.1 | |
| 8.3 |
| Embodied Energy, MJ/kg | 140 | |
| 150 |
| Embodied Water, L/kg | 1110 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 31 to 34 | |
| 0.68 to 7.0 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1270 to 1440 | |
| 28 to 280 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 45 | |
| 51 |
| Strength to Weight: Axial, points | 46 to 47 | |
| 8.6 to 21 |
| Strength to Weight: Bending, points | 46 to 47 | |
| 16 to 29 |
| Thermal Diffusivity, mm2/s | 51 | |
| 81 |
| Thermal Shock Resistance, points | 22 to 23 | |
| 3.8 to 9.4 |
Alloy Composition
| Aluminum (Al), % | 85.7 to 89.5 | |
| 96 to 99.4 |
| Chromium (Cr), % | 0.1 to 0.22 | |
| 0 |
| Copper (Cu), % | 1.2 to 1.9 | |
| 0 to 0.5 |
| Iron (Fe), % | 0 to 0.35 | |
| 0 |
| Magnesium (Mg), % | 2.0 to 2.9 | |
| 0.4 to 1.2 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0 |
| Silicon (Si), % | 0 to 0.25 | |
| 0.2 to 0.8 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 |
| Zinc (Zn), % | 7.2 to 8.2 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 1.5 |