7049A Aluminum vs. EN 1.4612 Stainless Steel
7049A aluminum belongs to the aluminum alloys classification, while EN 1.4612 stainless steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 7049A aluminum and the bottom bar is EN 1.4612 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 190 |
| Elongation at Break, % | 5.0 to 5.7 | |
| 11 |
| Fatigue Strength, MPa | 180 | |
| 860 to 950 |
| Poisson's Ratio | 0.32 | |
| 0.28 |
| Shear Modulus, GPa | 27 | |
| 76 |
| Shear Strength, MPa | 340 to 350 | |
| 1010 to 1110 |
| Tensile Strength: Ultimate (UTS), MPa | 580 to 590 | |
| 1690 to 1850 |
| Tensile Strength: Yield (Proof), MPa | 500 to 530 | |
| 1570 to 1730 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 790 |
| Melting Completion (Liquidus), °C | 640 | |
| 1450 |
| Melting Onset (Solidus), °C | 430 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 850 | |
| 480 |
| Thermal Expansion, µm/m-K | 24 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 16 |
| Density, g/cm3 | 3.1 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 3.6 |
| Embodied Energy, MJ/kg | 150 | |
| 50 |
| Embodied Water, L/kg | 1100 | |
| 140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 28 to 32 | |
| 190 to 210 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 44 | |
| 25 |
| Strength to Weight: Axial, points | 52 to 53 | |
| 60 to 65 |
| Strength to Weight: Bending, points | 50 to 51 | |
| 40 to 43 |
| Thermal Shock Resistance, points | 25 | |
| 58 to 63 |
Alloy Composition
| Aluminum (Al), % | 84.6 to 89.5 | |
| 1.4 to 1.8 |
| Carbon (C), % | 0 | |
| 0 to 0.015 |
| Chromium (Cr), % | 0.050 to 0.25 | |
| 11 to 12.5 |
| Copper (Cu), % | 1.2 to 1.9 | |
| 0 |
| Iron (Fe), % | 0 to 0.5 | |
| 71.5 to 75.5 |
| Magnesium (Mg), % | 2.1 to 3.1 | |
| 0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 0 | |
| 1.8 to 2.3 |
| Nickel (Ni), % | 0 | |
| 10.2 to 11.3 |
| Nitrogen (N), % | 0 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 | |
| 0 to 0.0050 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0.2 to 0.5 |
| Zinc (Zn), % | 7.2 to 8.4 | |
| 0 |
| Zirconium (Zr), % | 0 to 0.25 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 |