7076 Aluminum vs. 333.0 Aluminum
Both 7076 aluminum and 333.0 aluminum are aluminum alloys. They have 88% of their average alloy composition in common.
For each property being compared, the top bar is 7076 aluminum and the bottom bar is 333.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 | |
| 90 to 110 |
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 73 |
| Elongation at Break, % | 6.2 | |
| 1.0 to 2.0 |
| Fatigue Strength, MPa | 170 | |
| 83 to 100 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 28 |
| Shear Strength, MPa | 310 | |
| 190 to 230 |
| Tensile Strength: Ultimate (UTS), MPa | 530 | |
| 230 to 280 |
| Tensile Strength: Yield (Proof), MPa | 460 | |
| 130 to 210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 380 | |
| 520 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 170 |
| Melting Completion (Liquidus), °C | 630 | |
| 590 |
| Melting Onset (Solidus), °C | 460 | |
| 530 |
| Specific Heat Capacity, J/kg-K | 860 | |
| 880 |
| Thermal Conductivity, W/m-K | 140 | |
| 100 to 140 |
| Thermal Expansion, µm/m-K | 24 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 35 | |
| 26 to 35 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 100 | |
| 83 to 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 10 |
| Density, g/cm3 | 3.0 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 7.6 |
| Embodied Energy, MJ/kg | 150 | |
| 140 |
| Embodied Water, L/kg | 1110 | |
| 1040 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 31 | |
| 2.1 to 4.6 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1510 | |
| 120 to 290 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 45 | |
| 49 |
| Strength to Weight: Axial, points | 49 | |
| 22 to 27 |
| Strength to Weight: Bending, points | 48 | |
| 29 to 34 |
| Thermal Diffusivity, mm2/s | 54 | |
| 42 to 57 |
| Thermal Shock Resistance, points | 23 | |
| 11 to 13 |
Alloy Composition
| Aluminum (Al), % | 86.9 to 91.2 | |
| 81.8 to 89 |
| Copper (Cu), % | 0.3 to 1.0 | |
| 3.0 to 4.0 |
| Iron (Fe), % | 0 to 0.6 | |
| 0 to 1.0 |
| Magnesium (Mg), % | 1.2 to 2.0 | |
| 0.050 to 0.5 |
| Manganese (Mn), % | 0.3 to 0.8 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 0 to 0.5 |
| Silicon (Si), % | 0 to 0.4 | |
| 8.0 to 10 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 to 0.25 |
| Zinc (Zn), % | 7.0 to 8.0 | |
| 0 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.5 |