7076 Aluminum vs. EN 1.1152 Steel

7076 aluminum belongs to the aluminum alloys classification, while EN 1.1152 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 7076 aluminum and the bottom bar is EN 1.1152 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
120 to 160
Elastic (Young's, Tensile) Modulus, GPa 70
190
Elongation at Break, % 6.2
12 to 22
Fatigue Strength, MPa 170
190 to 300
Poisson's Ratio 0.32
0.29
Shear Modulus, GPa 27
73
Shear Strength, MPa 310
290 to 340
Tensile Strength: Ultimate (UTS), MPa 530
400 to 550
Tensile Strength: Yield (Proof), MPa 460
270 to 440

Thermal Properties

Latent Heat of Fusion, J/g 380
250
Maximum Temperature: Mechanical, °C 170
400
Melting Completion (Liquidus), °C 630
1460
Melting Onset (Solidus), °C 460
1420
Specific Heat Capacity, J/kg-K 860
470
Thermal Conductivity, W/m-K 140
52
Thermal Expansion, µm/m-K 24
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 35
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 100
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
1.8
Density, g/cm3 3.0
7.8
Embodied Carbon, kg CO2/kg material 8.0
1.4
Embodied Energy, MJ/kg 150
18
Embodied Water, L/kg 1110
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
41 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 1510
200 to 530
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 45
24
Strength to Weight: Axial, points 49
14 to 19
Strength to Weight: Bending, points 48
15 to 19
Thermal Diffusivity, mm2/s 54
14
Thermal Shock Resistance, points 23
13 to 17

Alloy Composition

Aluminum (Al), % 86.9 to 91.2
0
Carbon (C), % 0
0.18 to 0.22
Copper (Cu), % 0.3 to 1.0
0 to 0.25
Iron (Fe), % 0 to 0.6
98.6 to 99.52
Magnesium (Mg), % 1.2 to 2.0
0
Manganese (Mn), % 0.3 to 0.8
0.3 to 0.6
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.4
0 to 0.3
Sulfur (S), % 0
0 to 0.025
Titanium (Ti), % 0 to 0.2
0
Zinc (Zn), % 7.0 to 8.0
0
Residuals, % 0 to 0.15
0