7108A Aluminum vs. ASTM Grade HT Steel

7108A aluminum belongs to the aluminum alloys classification, while ASTM grade HT steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 7108A aluminum and the bottom bar is ASTM grade HT steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 69
190
Elongation at Break, % 11 to 13
4.6
Fatigue Strength, MPa 120 to 130
130
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 26
76
Tensile Strength: Ultimate (UTS), MPa 350
500
Tensile Strength: Yield (Proof), MPa 290 to 300
270

Thermal Properties

Latent Heat of Fusion, J/g 380
310
Maximum Temperature: Mechanical, °C 210
1010
Melting Completion (Liquidus), °C 630
1390
Melting Onset (Solidus), °C 520
1340
Specific Heat Capacity, J/kg-K 870
480
Thermal Conductivity, W/m-K 150
12
Thermal Expansion, µm/m-K 24
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 36
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 110
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 10
31
Density, g/cm3 2.9
8.0
Embodied Carbon, kg CO2/kg material 8.3
5.4
Embodied Energy, MJ/kg 150
76
Embodied Water, L/kg 1150
190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 38 to 44
19
Resilience: Unit (Modulus of Resilience), kJ/m3 610 to 640
180
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 47
24
Strength to Weight: Axial, points 33 to 34
18
Strength to Weight: Bending, points 38
18
Thermal Diffusivity, mm2/s 59
3.2
Thermal Shock Resistance, points 15 to 16
12

Alloy Composition

Aluminum (Al), % 91.6 to 94.4
0
Carbon (C), % 0
0.35 to 0.75
Chromium (Cr), % 0 to 0.040
15 to 19
Copper (Cu), % 0 to 0.050
0
Gallium (Ga), % 0 to 0.030
0
Iron (Fe), % 0 to 0.3
38.2 to 51.7
Magnesium (Mg), % 0.7 to 1.5
0
Manganese (Mn), % 0 to 0.050
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0
33 to 37
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.2
0 to 2.5
Sulfur (S), % 0
0 to 0.040
Titanium (Ti), % 0 to 0.030
0
Zinc (Zn), % 4.8 to 5.8
0
Zirconium (Zr), % 0.15 to 0.25
0
Residuals, % 0 to 0.15
0