7108A Aluminum vs. EN-MC21110 Magnesium
7108A aluminum belongs to the aluminum alloys classification, while EN-MC21110 magnesium belongs to the magnesium alloys. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 7108A aluminum and the bottom bar is EN-MC21110 magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 46 |
| Elongation at Break, % | 11 to 13 | |
| 2.8 to 6.7 |
| Fatigue Strength, MPa | 120 to 130 | |
| 75 to 78 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 26 | |
| 18 |
| Shear Strength, MPa | 210 | |
| 120 to 160 |
| Tensile Strength: Ultimate (UTS), MPa | 350 | |
| 200 to 270 |
| Tensile Strength: Yield (Proof), MPa | 290 to 300 | |
| 100 to 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 380 | |
| 350 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 130 |
| Melting Completion (Liquidus), °C | 630 | |
| 600 |
| Melting Onset (Solidus), °C | 520 | |
| 500 |
| Specific Heat Capacity, J/kg-K | 870 | |
| 990 |
| Thermal Conductivity, W/m-K | 150 | |
| 80 |
| Thermal Expansion, µm/m-K | 24 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 36 | |
| 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
| 61 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 12 |
| Density, g/cm3 | 2.9 | |
| 1.7 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 23 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1150 | |
| 990 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 38 to 44 | |
| 4.9 to 14 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 610 to 640 | |
| 120 to 150 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 47 | |
| 69 |
| Strength to Weight: Axial, points | 33 to 34 | |
| 33 to 44 |
| Strength to Weight: Bending, points | 38 | |
| 45 to 54 |
| Thermal Diffusivity, mm2/s | 59 | |
| 47 |
| Thermal Shock Resistance, points | 15 to 16 | |
| 12 to 16 |
Alloy Composition
| Aluminum (Al), % | 91.6 to 94.4 | |
| 7.0 to 8.7 |
| Chromium (Cr), % | 0 to 0.040 | |
| 0 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 to 0.030 |
| Gallium (Ga), % | 0 to 0.030 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 0 to 0.0050 |
| Magnesium (Mg), % | 0.7 to 1.5 | |
| 89.6 to 92.6 |
| Manganese (Mn), % | 0 to 0.050 | |
| 0.1 to 0.35 |
| Nickel (Ni), % | 0 | |
| 0 to 0.0020 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 0.2 |
| Titanium (Ti), % | 0 to 0.030 | |
| 0 |
| Zinc (Zn), % | 4.8 to 5.8 | |
| 0.35 to 1.0 |
| Zirconium (Zr), % | 0.15 to 0.25 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.010 |