7129 Aluminum vs. 3105 Aluminum
Both 7129 Aluminum and 3105 aluminum are aluminum alloys. They have a moderately high 94% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is 7129 Aluminum and the bottom bar is 3105 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 69 |
| Elongation at Break, % | 9.0 to 9.1 | |
| 1.1 to 20 |
| Fatigue Strength, MPa | 150 to 190 | |
| 39 to 95 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 250 to 260 | |
| 77 to 140 |
| Tensile Strength: Ultimate (UTS), MPa | 430 | |
| 120 to 240 |
| Tensile Strength: Yield (Proof), MPa | 380 to 390 | |
| 46 to 220 |
Thermal Properties
| Latent Heat of Fusion, J/g | 380 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 180 |
| Melting Completion (Liquidus), °C | 630 | |
| 660 |
| Melting Onset (Solidus), °C | 510 | |
| 640 |
| Specific Heat Capacity, J/kg-K | 880 | |
| 900 |
| Thermal Conductivity, W/m-K | 150 | |
| 170 |
| Thermal Expansion, µm/m-K | 24 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 40 | |
| 44 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 140 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.9 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 8.2 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1150 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 37 to 38 | |
| 2.6 to 19 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1050 to 1090 | |
| 15 to 340 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 47 | |
| 50 |
| Strength to Weight: Axial, points | 41 | |
| 12 to 24 |
| Strength to Weight: Bending, points | 43 to 44 | |
| 20 to 31 |
| Thermal Diffusivity, mm2/s | 58 | |
| 68 |
| Thermal Shock Resistance, points | 19 | |
| 5.2 to 11 |
Alloy Composition
| Aluminum (Al), % | 91 to 94 | |
| 96 to 99.5 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 to 0.2 |
| Copper (Cu), % | 0.5 to 0.9 | |
| 0 to 0.3 |
| Gallium (Ga), % | 0 to 0.030 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 0 to 0.7 |
| Magnesium (Mg), % | 1.3 to 2.0 | |
| 0.2 to 0.8 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0.3 to 0.8 |
| Silicon (Si), % | 0 to 0.15 | |
| 0 to 0.6 |
| Titanium (Ti), % | 0 to 0.050 | |
| 0 to 0.1 |
| Vanadium (V), % | 0 to 0.050 | |
| 0 |
| Zinc (Zn), % | 4.2 to 5.2 | |
| 0 to 0.4 |
| Residuals, % | 0 | |
| 0 to 0.15 |