7178 Aluminum vs. SAE-AISI H41 Steel

7178 aluminum belongs to the aluminum alloys classification, while SAE-AISI H41 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 7178 aluminum and the bottom bar is SAE-AISI H41 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
200
Poisson's Ratio 0.32
0.29
Shear Modulus, GPa 27
77
Tensile Strength: Ultimate (UTS), MPa 240 to 640
710 to 2210

Thermal Properties

Latent Heat of Fusion, J/g 370
270
Melting Completion (Liquidus), °C 630
1560
Melting Onset (Solidus), °C 480
1510
Specific Heat Capacity, J/kg-K 860
450
Thermal Conductivity, W/m-K 130
28
Thermal Expansion, µm/m-K 23
12

Otherwise Unclassified Properties

Base Metal Price, % relative 10
18
Density, g/cm3 3.1
8.1
Embodied Carbon, kg CO2/kg material 8.2
6.8
Embodied Energy, MJ/kg 150
97
Embodied Water, L/kg 1110
97

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 45
24
Strength to Weight: Axial, points 21 to 58
24 to 76
Strength to Weight: Bending, points 28 to 54
22 to 47
Thermal Diffusivity, mm2/s 47
7.7
Thermal Shock Resistance, points 10 to 28
20 to 64

Alloy Composition

Aluminum (Al), % 85.4 to 89.5
0
Carbon (C), % 0
0.6 to 0.75
Chromium (Cr), % 0.18 to 0.28
3.5 to 4.0
Copper (Cu), % 1.6 to 2.4
0
Iron (Fe), % 0 to 0.5
81.8 to 85
Magnesium (Mg), % 2.4 to 3.1
0
Manganese (Mn), % 0 to 0.3
0.15 to 0.4
Molybdenum (Mo), % 0
8.2 to 9.2
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.4
0.2 to 0.45
Sulfur (S), % 0
0 to 0.030
Titanium (Ti), % 0 to 0.2
0
Tungsten (W), % 0
1.4 to 2.1
Vanadium (V), % 0
1.0 to 1.3
Zinc (Zn), % 6.3 to 7.3
0
Residuals, % 0 to 0.15
0

Comparable Variants