7204 Aluminum vs. 5052 Aluminum
Both 7204 aluminum and 5052 aluminum are aluminum alloys. They have a moderately high 95% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is 7204 aluminum and the bottom bar is 5052 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 68 |
| Elongation at Break, % | 11 to 13 | |
| 1.1 to 22 |
| Fatigue Strength, MPa | 110 to 130 | |
| 66 to 140 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 130 to 220 | |
| 120 to 180 |
| Tensile Strength: Ultimate (UTS), MPa | 220 to 380 | |
| 190 to 320 |
| Tensile Strength: Yield (Proof), MPa | 120 to 310 | |
| 75 to 280 |
Thermal Properties
| Latent Heat of Fusion, J/g | 380 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 190 |
| Melting Completion (Liquidus), °C | 640 | |
| 650 |
| Melting Onset (Solidus), °C | 520 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 880 | |
| 900 |
| Thermal Conductivity, W/m-K | 150 | |
| 140 |
| Thermal Expansion, µm/m-K | 24 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 39 | |
| 35 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.9 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.4 | |
| 8.6 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1140 | |
| 1190 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 25 to 40 | |
| 1.7 to 69 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 to 710 | |
| 41 to 590 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 47 | |
| 50 |
| Strength to Weight: Axial, points | 21 to 36 | |
| 19 to 33 |
| Strength to Weight: Bending, points | 28 to 40 | |
| 27 to 38 |
| Thermal Diffusivity, mm2/s | 58 | |
| 57 |
| Thermal Shock Resistance, points | 9.4 to 16 | |
| 8.3 to 14 |
Alloy Composition
| Aluminum (Al), % | 90.5 to 94.8 | |
| 95.8 to 97.7 |
| Chromium (Cr), % | 0 to 0.3 | |
| 0.15 to 0.35 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.35 | |
| 0 to 0.4 |
| Magnesium (Mg), % | 1.0 to 2.0 | |
| 2.2 to 2.8 |
| Manganese (Mn), % | 0.2 to 0.7 | |
| 0 to 0.1 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 0.25 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 |
| Vanadium (V), % | 0 to 0.1 | |
| 0 |
| Zinc (Zn), % | 4.0 to 5.0 | |
| 0 to 0.1 |
| Zirconium (Zr), % | 0 to 0.25 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.15 |