7475 Aluminum vs. 2014 Aluminum
Both 7475 aluminum and 2014 aluminum are aluminum alloys. They have a moderately high 93% of their average alloy composition in common.
For each property being compared, the top bar is 7475 aluminum and the bottom bar is 2014 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 72 |
| Elongation at Break, % | 10 to 12 | |
| 1.5 to 16 |
| Fatigue Strength, MPa | 190 to 210 | |
| 90 to 160 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 27 |
| Shear Strength, MPa | 320 to 350 | |
| 130 to 290 |
| Tensile Strength: Ultimate (UTS), MPa | 530 to 590 | |
| 190 to 500 |
| Tensile Strength: Yield (Proof), MPa | 440 to 520 | |
| 100 to 440 |
Thermal Properties
| Latent Heat of Fusion, J/g | 380 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 210 |
| Melting Completion (Liquidus), °C | 640 | |
| 630 |
| Melting Onset (Solidus), °C | 480 | |
| 510 |
| Specific Heat Capacity, J/kg-K | 870 | |
| 870 |
| Thermal Conductivity, W/m-K | 140 to 160 | |
| 150 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 33 to 42 | |
| 40 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 98 to 120 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 11 |
| Density, g/cm3 | 3.0 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 8.1 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1130 | |
| 1130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 53 to 68 | |
| 6.6 to 56 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1390 to 1920 | |
| 76 to 1330 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 46 | |
| 46 |
| Strength to Weight: Axial, points | 49 to 55 | |
| 18 to 46 |
| Strength to Weight: Bending, points | 48 to 52 | |
| 25 to 46 |
| Thermal Diffusivity, mm2/s | 53 to 63 | |
| 58 |
| Thermal Shock Resistance, points | 23 to 26 | |
| 8.4 to 22 |
Alloy Composition
| Aluminum (Al), % | 88.6 to 91.6 | |
| 90.4 to 95 |
| Chromium (Cr), % | 0.18 to 0.25 | |
| 0 to 0.1 |
| Copper (Cu), % | 1.2 to 1.9 | |
| 3.9 to 5.0 |
| Iron (Fe), % | 0 to 0.12 | |
| 0 to 0.7 |
| Magnesium (Mg), % | 1.9 to 2.6 | |
| 0.2 to 0.8 |
| Manganese (Mn), % | 0 to 0.060 | |
| 0.4 to 1.2 |
| Silicon (Si), % | 0 to 0.1 | |
| 0.5 to 1.2 |
| Titanium (Ti), % | 0 to 0.060 | |
| 0 to 0.15 |
| Zinc (Zn), % | 5.1 to 6.2 | |
| 0 to 0.25 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.15 |