80-silver 20-cadmium-oxide vs. AISI 204 Stainless Steel
80-silver 20-cadmium-oxide belongs to the otherwise unclassified metals classification, while AISI 204 stainless steel belongs to the iron alloys. There are 8 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is 80-silver 20-cadmium-oxide and the bottom bar is AISI 204 stainless steel.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 9.9 | |
| 7.7 |
| Electrical Conductivity: Equal Volume, % IACS | 63 to 77 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 57 to 70 | |
| 2.9 |
| Elongation at Break, % | 1.1 to 15 | |
| 23 to 39 |
| Shear Strength, MPa | 190 to 220 | |
| 500 to 700 |
| Strength to Weight: Axial, points | 8.8 to 12 | |
| 27 to 40 |
| Strength to Weight: Bending, points | 10 to 13 | |
| 24 to 31 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 440 | |
| 730 to 1100 |