80-silver 20-cadmium-oxide vs. Solder Alloy 104
Both 80-silver 20-cadmium-oxide and solder alloy 104 are otherwise unclassified metals. There are 7 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is 80-silver 20-cadmium-oxide and the bottom bar is solder alloy 104.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 9.9 | |
| 8.9 |
| Electrical Conductivity: Equal Volume, % IACS | 63 to 77 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 57 to 70 | |
| 11 |
| Elongation at Break, % | 1.1 to 15 | |
| 46 |
| Strength to Weight: Axial, points | 8.8 to 12 | |
| 1.6 |
| Strength to Weight: Bending, points | 10 to 13 | |
| 3.4 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 440 | |
| 51 |