85-platinum 15-iridium vs. Grade 200 Maraging Steel
85-platinum 15-iridium belongs to the otherwise unclassified metals classification, while grade 200 maraging steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 85-platinum 15-iridium and the bottom bar is grade 200 maraging steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Elongation at Break, % | 5.5 to 34 | |
| 9.1 to 18 |
| Poisson's Ratio | 0.38 | |
| 0.3 |
| Shear Modulus, GPa | 81 | |
| 74 |
| Shear Strength, MPa | 370 to 420 | |
| 600 to 890 |
| Tensile Strength: Ultimate (UTS), MPa | 560 to 730 | |
| 970 to 1500 |
Thermal Properties
| Latent Heat of Fusion, J/g | 110 | |
| 260 |
| Melting Completion (Liquidus), °C | 1820 | |
| 1460 |
| Melting Onset (Solidus), °C | 1790 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 130 | |
| 460 |
| Thermal Expansion, µm/m-K | 8.4 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 22 | |
| 8.2 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.7 | |
| 13 |
| Stiffness to Weight: Bending, points | 9.3 | |
| 23 |
| Strength to Weight: Axial, points | 7.1 to 9.3 | |
| 33 to 51 |
| Strength to Weight: Bending, points | 6.9 to 8.3 | |
| 27 to 35 |
| Thermal Shock Resistance, points | 21 to 28 | |
| 29 to 45 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.050 to 0.15 |
| Boron (B), % | 0 | |
| 0 to 0.0030 |
| Calcium (Ca), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Cobalt (Co), % | 0 | |
| 8.0 to 9.0 |
| Iridium (Ir), % | 14.5 to 15.5 | |
| 0 |
| Iron (Fe), % | 0 | |
| 67.8 to 71.8 |
| Manganese (Mn), % | 0 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 0 | |
| 3.0 to 3.5 |
| Nickel (Ni), % | 0 | |
| 17 to 19 |
| Phosphorus (P), % | 0 | |
| 0 to 0.010 |
| Platinum (Pt), % | 84.3 to 85.5 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0.15 to 0.25 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.020 |
| Residuals, % | 0 to 0.2 | |
| 0 |