85-silver 15-cadmium-oxide vs. AISI 410Cb Stainless Steel
85-silver 15-cadmium-oxide belongs to the otherwise unclassified metals classification, while AISI 410Cb stainless steel belongs to the iron alloys. There are 8 material properties with values for both materials. Properties with values for just one material (26, in this case) are not shown.
For each property being compared, the top bar is 85-silver 15-cadmium-oxide and the bottom bar is AISI 410Cb stainless steel.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 10 | |
| 7.7 |
| Electrical Conductivity: Equal Volume, % IACS | 64 to 82 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 57 to 73 | |
| 3.3 |
| Elongation at Break, % | 2.2 to 16 | |
| 15 |
| Shear Strength, MPa | 180 to 210 | |
| 340 to 590 |
| Strength to Weight: Axial, points | 8.1 to 12 | |
| 20 to 35 |
| Strength to Weight: Bending, points | 9.7 to 13 | |
| 19 to 28 |
| Tensile Strength: Ultimate (UTS), MPa | 290 to 440 | |
| 550 to 960 |