86.5-silver 13.5-cadmium-oxide vs. Solder Alloy 201
Both 86.5-silver 13.5-cadmium-oxide and solder alloy 201 are otherwise unclassified metals. There are 7 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is 86.5-silver 13.5-cadmium-oxide and the bottom bar is solder alloy 201.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 10 | |
| 7.3 |
| Electrical Conductivity: Equal Volume, % IACS | 72 to 85 | |
| 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 64 to 76 | |
| 15 |
| Elongation at Break, % | 3.4 to 16 | |
| 38 |
| Strength to Weight: Axial, points | 7.6 to 11 | |
| 1.6 |
| Strength to Weight: Bending, points | 9.3 to 12 | |
| 3.6 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 410 | |
| 41 |