86.5-silver 13.5-cadmium-oxide vs. K94200 Alloy
86.5-silver 13.5-cadmium-oxide belongs to the otherwise unclassified metals classification, while K94200 alloy belongs to the iron alloys. There are 8 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is 86.5-silver 13.5-cadmium-oxide and the bottom bar is K94200 alloy.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 10 | |
| 8.2 |
| Electrical Conductivity: Equal Volume, % IACS | 72 to 85 | |
| 2.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 64 to 76 | |
| 3.0 |
| Elongation at Break, % | 3.4 to 16 | |
| 5.0 to 32 |
| Shear Strength, MPa | 170 to 210 | |
| 330 to 410 |
| Strength to Weight: Axial, points | 7.6 to 11 | |
| 17 to 24 |
| Strength to Weight: Bending, points | 9.3 to 12 | |
| 17 to 22 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 410 | |
| 500 to 710 |