88-silver 12-tin-oxide vs. 4007 Aluminum
88-silver 12-tin-oxide belongs to the otherwise unclassified metals classification, while 4007 aluminum belongs to the aluminum alloys. There are 6 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is 88-silver 12-tin-oxide and the bottom bar is 4007 aluminum.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 84 to 86 | |
| 42 |
| Elongation at Break, % | 9.0 to 37 | |
| 5.1 to 23 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 to 70 | |
| 7.4 to 23 |
| Shear Strength, MPa | 150 to 160 | |
| 80 to 90 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 280 | |
| 130 to 160 |
| Tensile Strength: Yield (Proof), MPa | 110 to 260 | |
| 50 to 120 |