88-silver 12-tin-oxide vs. AISI 204 Stainless Steel
88-silver 12-tin-oxide belongs to the otherwise unclassified metals classification, while AISI 204 stainless steel belongs to the iron alloys. There are 6 material properties with values for both materials. Properties with values for just one material (27, in this case) are not shown.
For each property being compared, the top bar is 88-silver 12-tin-oxide and the bottom bar is AISI 204 stainless steel.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 84 to 86 | |
| 2.4 |
| Elongation at Break, % | 9.0 to 37 | |
| 23 to 39 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 to 70 | |
| 240 to 250 |
| Shear Strength, MPa | 150 to 160 | |
| 500 to 700 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 280 | |
| 730 to 1100 |
| Tensile Strength: Yield (Proof), MPa | 110 to 260 | |
| 380 to 1080 |