88-silver 12-tin-oxide vs. AISI 205 Stainless Steel
88-silver 12-tin-oxide belongs to the otherwise unclassified metals classification, while AISI 205 stainless steel belongs to the iron alloys. There are 5 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is 88-silver 12-tin-oxide and the bottom bar is AISI 205 stainless steel.
Metric UnitsUS Customary Units
Material Properties
| Elongation at Break, % | 9.0 to 37 | |
| 11 to 51 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 to 70 | |
| 150 to 430 |
| Shear Strength, MPa | 150 to 160 | |
| 560 to 850 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 280 | |
| 800 to 1430 |
| Tensile Strength: Yield (Proof), MPa | 110 to 260 | |
| 450 to 1100 |