88-silver 12-tin-oxide vs. Nickel 201
88-silver 12-tin-oxide belongs to the otherwise unclassified metals classification, while nickel 201 belongs to the nickel alloys. There are 6 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is 88-silver 12-tin-oxide and the bottom bar is nickel 201.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 84 to 86 | |
| 19 |
| Elongation at Break, % | 9.0 to 37 | |
| 4.5 to 45 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 to 70 | |
| 25 to 130 |
| Shear Strength, MPa | 150 to 160 | |
| 270 to 380 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 280 | |
| 390 to 660 |
| Tensile Strength: Yield (Proof), MPa | 110 to 260 | |
| 80 to 510 |