88-silver 12-tin-oxide vs. Nickel 625
88-silver 12-tin-oxide belongs to the otherwise unclassified metals classification, while nickel 625 belongs to the nickel alloys. There are 6 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is 88-silver 12-tin-oxide and the bottom bar is nickel 625.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 84 to 86 | |
| 1.3 |
| Elongation at Break, % | 9.0 to 37 | |
| 33 to 34 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 to 70 | |
| 220 to 250 |
| Shear Strength, MPa | 150 to 160 | |
| 530 to 600 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 280 | |
| 790 to 910 |
| Tensile Strength: Yield (Proof), MPa | 110 to 260 | |
| 320 to 450 |