88-silver 12-tin-oxide vs. C19700 Copper
88-silver 12-tin-oxide belongs to the otherwise unclassified metals classification, while C19700 copper belongs to the copper alloys. There are 6 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is 88-silver 12-tin-oxide and the bottom bar is C19700 copper.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 84 to 86 | |
| 86 to 88 |
| Elongation at Break, % | 9.0 to 37 | |
| 2.4 to 13 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 to 70 | |
| 12 to 49 |
| Shear Strength, MPa | 150 to 160 | |
| 240 to 300 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 280 | |
| 400 to 530 |
| Tensile Strength: Yield (Proof), MPa | 110 to 260 | |
| 330 to 520 |