88-silver 12-tin-oxide vs. C61900 Bronze
88-silver 12-tin-oxide belongs to the otherwise unclassified metals classification, while C61900 bronze belongs to the copper alloys. There are 6 material properties with values for both materials. Properties with values for just one material (23, in this case) are not shown.
For each property being compared, the top bar is 88-silver 12-tin-oxide and the bottom bar is C61900 bronze.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 84 to 86 | |
| 11 |
| Elongation at Break, % | 9.0 to 37 | |
| 21 to 32 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 to 70 | |
| 110 to 150 |
| Shear Strength, MPa | 150 to 160 | |
| 370 to 410 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 280 | |
| 570 to 650 |
| Tensile Strength: Yield (Proof), MPa | 110 to 260 | |
| 230 to 310 |