88-silver 12-tin-oxide vs. S21904 Stainless Steel
88-silver 12-tin-oxide belongs to the otherwise unclassified metals classification, while S21904 stainless steel belongs to the iron alloys. There are 6 material properties with values for both materials. Properties with values for just one material (27, in this case) are not shown.
For each property being compared, the top bar is 88-silver 12-tin-oxide and the bottom bar is S21904 stainless steel.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 84 to 86 | |
| 2.5 |
| Elongation at Break, % | 9.0 to 37 | |
| 17 to 51 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 to 70 | |
| 160 to 310 |
| Shear Strength, MPa | 150 to 160 | |
| 510 to 620 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 280 | |
| 700 to 1000 |
| Tensile Strength: Yield (Proof), MPa | 110 to 260 | |
| 390 to 910 |