88-silver 12-tin-oxide vs. ZA-27
88-silver 12-tin-oxide belongs to the otherwise unclassified metals classification, while ZA-27 belongs to the zinc alloys. There are 6 material properties with values for both materials. Properties with values for just one material (30, in this case) are not shown.
For each property being compared, the top bar is 88-silver 12-tin-oxide and the bottom bar is ZA-27.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 84 to 86 | |
| 30 |
| Elongation at Break, % | 9.0 to 37 | |
| 2.0 to 4.5 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 to 70 | |
| 8.1 to 18 |
| Shear Strength, MPa | 150 to 160 | |
| 230 to 330 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 280 | |
| 400 to 430 |
| Tensile Strength: Yield (Proof), MPa | 110 to 260 | |
| 260 to 370 |