90-silver 10-cadmium-oxide vs. AISI 204 Stainless Steel
90-silver 10-cadmium-oxide belongs to the otherwise unclassified metals classification, while AISI 204 stainless steel belongs to the iron alloys. There are 8 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is 90-silver 10-cadmium-oxide and the bottom bar is AISI 204 stainless steel.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 10 | |
| 7.7 |
| Electrical Conductivity: Equal Volume, % IACS | 72 to 100 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 64 to 91 | |
| 2.9 |
| Elongation at Break, % | 1.1 to 28 | |
| 23 to 39 |
| Shear Strength, MPa | 170 to 230 | |
| 500 to 700 |
| Strength to Weight: Axial, points | 7.0 to 11 | |
| 27 to 40 |
| Strength to Weight: Bending, points | 8.8 to 12 | |
| 24 to 31 |
| Tensile Strength: Ultimate (UTS), MPa | 260 to 400 | |
| 730 to 1100 |