90-silver 10-cadmium-oxide vs. Automotive Malleable Cast Iron
90-silver 10-cadmium-oxide belongs to the otherwise unclassified metals classification, while automotive malleable cast iron belongs to the iron alloys. There are 7 material properties with values for both materials. Properties with values for just one material (22, in this case) are not shown.
For each property being compared, the top bar is 90-silver 10-cadmium-oxide and the bottom bar is automotive malleable cast iron.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 10 | |
| 7.6 |
| Electrical Conductivity: Equal Volume, % IACS | 72 to 100 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 64 to 91 | |
| 8.7 |
| Elongation at Break, % | 1.1 to 28 | |
| 1.0 to 10 |
| Strength to Weight: Axial, points | 7.0 to 11 | |
| 13 to 26 |
| Strength to Weight: Bending, points | 8.8 to 12 | |
| 14 to 24 |
| Tensile Strength: Ultimate (UTS), MPa | 260 to 400 | |
| 350 to 720 |