90-silver 10-nickel vs. EN 1.8201 Steel
90-silver 10-nickel belongs to the otherwise unclassified metals classification, while EN 1.8201 steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is 90-silver 10-nickel and the bottom bar is EN 1.8201 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 82 | |
| 190 |
| Poisson's Ratio | 0.36 | |
| 0.29 |
| Shear Modulus, GPa | 30 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 250 to 420 | |
| 630 |
Thermal Properties
| Latent Heat of Fusion, J/g | 130 | |
| 250 |
| Melting Completion (Liquidus), °C | 840 | |
| 1500 |
| Melting Onset (Solidus), °C | 960 | |
| 1450 |
| Specific Heat Capacity, J/kg-K | 260 | |
| 470 |
| Thermal Expansion, µm/m-K | 19 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 90 | |
| 7.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 79 | |
| 8.8 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 8.0 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.4 | |
| 13 |
| Stiffness to Weight: Bending, points | 14 | |
| 24 |
| Strength to Weight: Axial, points | 6.7 to 11 | |
| 22 |
| Strength to Weight: Bending, points | 8.5 to 12 | |
| 20 |
| Thermal Shock Resistance, points | 11 to 19 | |
| 18 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.030 |
| Boron (B), % | 0 | |
| 0.0010 to 0.0060 |
| Carbon (C), % | 0 | |
| 0.040 to 0.1 |
| Chromium (Cr), % | 0 | |
| 1.9 to 2.6 |
| Iron (Fe), % | 0 | |
| 93.6 to 96.2 |
| Manganese (Mn), % | 0 | |
| 0.1 to 0.6 |
| Molybdenum (Mo), % | 0 | |
| 0.050 to 0.3 |
| Nickel (Ni), % | 8.8 to 11 | |
| 0 |
| Niobium (Nb), % | 0 | |
| 0.020 to 0.080 |
| Nitrogen (N), % | 0 | |
| 0 to 0.015 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Silver (Ag), % | 89 to 91 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0.0050 to 0.060 |
| Tungsten (W), % | 0 | |
| 1.5 to 1.8 |
| Vanadium (V), % | 0 | |
| 0.2 to 0.3 |
| Residuals, % | 0 to 0.2 | |
| 0 |