90-silver 10-nickel vs. SAE-AISI H19 Steel
90-silver 10-nickel belongs to the otherwise unclassified metals classification, while SAE-AISI H19 steel belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is 90-silver 10-nickel and the bottom bar is SAE-AISI H19 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 82 | |
| 190 |
| Poisson's Ratio | 0.36 | |
| 0.29 |
| Shear Modulus, GPa | 30 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 250 to 420 | |
| 720 to 1990 |
Thermal Properties
| Latent Heat of Fusion, J/g | 130 | |
| 260 |
| Melting Completion (Liquidus), °C | 840 | |
| 1540 |
| Melting Onset (Solidus), °C | 960 | |
| 1490 |
| Specific Heat Capacity, J/kg-K | 260 | |
| 460 |
| Thermal Expansion, µm/m-K | 19 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 8.2 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.4 | |
| 13 |
| Stiffness to Weight: Bending, points | 14 | |
| 24 |
| Strength to Weight: Axial, points | 6.7 to 11 | |
| 24 to 68 |
| Strength to Weight: Bending, points | 8.5 to 12 | |
| 22 to 43 |
| Thermal Shock Resistance, points | 11 to 19 | |
| 21 to 59 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0.32 to 0.45 |
| Chromium (Cr), % | 0 | |
| 4.0 to 4.8 |
| Cobalt (Co), % | 0 | |
| 4.0 to 4.5 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 | |
| 81.4 to 85.5 |
| Manganese (Mn), % | 0 | |
| 0.2 to 0.5 |
| Molybdenum (Mo), % | 0 | |
| 0.3 to 0.55 |
| Nickel (Ni), % | 8.8 to 11 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0.2 to 0.5 |
| Silver (Ag), % | 89 to 91 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 3.8 to 4.5 |
| Vanadium (V), % | 0 | |
| 1.8 to 2.2 |
| Residuals, % | 0 to 0.2 | |
| 0 |