90-silver 10-nickel vs. SAE-AISI M48 Steel
90-silver 10-nickel belongs to the otherwise unclassified metals classification, while SAE-AISI M48 steel belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is 90-silver 10-nickel and the bottom bar is SAE-AISI M48 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 82 | |
| 200 |
| Poisson's Ratio | 0.36 | |
| 0.29 |
| Shear Modulus, GPa | 30 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 250 to 420 | |
| 890 to 2390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 130 | |
| 260 |
| Melting Completion (Liquidus), °C | 840 | |
| 1670 |
| Melting Onset (Solidus), °C | 960 | |
| 1620 |
| Specific Heat Capacity, J/kg-K | 260 | |
| 420 |
| Thermal Expansion, µm/m-K | 19 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 8.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.4 | |
| 13 |
| Stiffness to Weight: Bending, points | 14 | |
| 22 |
| Strength to Weight: Axial, points | 6.7 to 11 | |
| 28 to 76 |
| Strength to Weight: Bending, points | 8.5 to 12 | |
| 23 to 45 |
| Thermal Shock Resistance, points | 11 to 19 | |
| 26 to 71 |
Alloy Composition
| Carbon (C), % | 0 | |
| 1.4 to 1.5 |
| Chromium (Cr), % | 0 | |
| 3.5 to 4.0 |
| Cobalt (Co), % | 0 | |
| 8.0 to 10 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 | |
| 63.8 to 69.8 |
| Manganese (Mn), % | 0 | |
| 0.15 to 0.4 |
| Molybdenum (Mo), % | 0 | |
| 4.8 to 5.5 |
| Nickel (Ni), % | 8.8 to 11 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0.15 to 0.4 |
| Silver (Ag), % | 89 to 91 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 9.5 to 10.5 |
| Vanadium (V), % | 0 | |
| 2.8 to 3.3 |
| Residuals, % | 0 to 0.2 | |
| 0 |