90-silver 10-nickel vs. C34500 Brass
90-silver 10-nickel belongs to the otherwise unclassified metals classification, while C34500 brass belongs to the copper alloys. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is 90-silver 10-nickel and the bottom bar is C34500 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 82 | |
| 100 |
| Poisson's Ratio | 0.36 | |
| 0.31 |
| Shear Modulus, GPa | 30 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 250 to 420 | |
| 340 to 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 130 | |
| 170 |
| Melting Completion (Liquidus), °C | 840 | |
| 910 |
| Melting Onset (Solidus), °C | 960 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 260 | |
| 380 |
| Thermal Expansion, µm/m-K | 19 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 90 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 79 | |
| 29 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 8.2 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.4 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 14 | |
| 19 |
| Strength to Weight: Axial, points | 6.7 to 11 | |
| 12 to 15 |
| Strength to Weight: Bending, points | 8.5 to 12 | |
| 13 to 16 |
| Thermal Shock Resistance, points | 11 to 19 | |
| 11 to 14 |
Alloy Composition
| Copper (Cu), % | 0 | |
| 62 to 65 |
| Iron (Fe), % | 0 | |
| 0 to 0.15 |
| Lead (Pb), % | 0 | |
| 1.5 to 2.5 |
| Nickel (Ni), % | 8.8 to 11 | |
| 0 |
| Silver (Ag), % | 89 to 91 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 32 to 36.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |