90-silver 10-tin-oxide vs. 1100 Aluminum
90-silver 10-tin-oxide belongs to the otherwise unclassified metals classification, while 1100 aluminum belongs to the aluminum alloys. There are 6 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is 90-silver 10-tin-oxide and the bottom bar is 1100 aluminum.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 77 to 82 | |
| 59 |
| Elongation at Break, % | 7.0 to 35 | |
| 1.1 to 32 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 20 to 68 | |
| 0.76 to 52 |
| Shear Strength, MPa | 160 to 170 | |
| 54 to 95 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 300 | |
| 86 to 170 |
| Tensile Strength: Yield (Proof), MPa | 120 to 280 | |
| 28 to 150 |