90-silver 10-tin-oxide vs. 356.0 Aluminum
90-silver 10-tin-oxide belongs to the otherwise unclassified metals classification, while 356.0 aluminum belongs to the aluminum alloys. There are 6 material properties with values for both materials. Properties with values for just one material (27, in this case) are not shown.
For each property being compared, the top bar is 90-silver 10-tin-oxide and the bottom bar is 356.0 aluminum.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 77 to 82 | |
| 40 to 43 |
| Elongation at Break, % | 7.0 to 35 | |
| 2.0 to 3.8 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 20 to 68 | |
| 3.2 to 8.2 |
| Shear Strength, MPa | 160 to 170 | |
| 140 to 190 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 300 | |
| 160 to 240 |
| Tensile Strength: Yield (Proof), MPa | 120 to 280 | |
| 100 to 190 |