90-silver 10-tin-oxide vs. 6013 Aluminum
90-silver 10-tin-oxide belongs to the otherwise unclassified metals classification, while 6013 aluminum belongs to the aluminum alloys. There are 6 material properties with values for both materials. Properties with values for just one material (24, in this case) are not shown.
For each property being compared, the top bar is 90-silver 10-tin-oxide and the bottom bar is 6013 aluminum.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 77 to 82 | |
| 38 |
| Elongation at Break, % | 7.0 to 35 | |
| 3.4 to 22 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 20 to 68 | |
| 13 to 58 |
| Shear Strength, MPa | 160 to 170 | |
| 190 to 240 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 300 | |
| 310 to 410 |
| Tensile Strength: Yield (Proof), MPa | 120 to 280 | |
| 170 to 350 |