90-silver 10-tin-oxide vs. ASTM A227 Spring Steel
90-silver 10-tin-oxide belongs to the otherwise unclassified metals classification, while ASTM A227 spring steel belongs to the iron alloys. There are 6 material properties with values for both materials. Properties with values for just one material (24, in this case) are not shown.
For each property being compared, the top bar is 90-silver 10-tin-oxide and the bottom bar is ASTM A227 spring steel.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 77 to 82 | |
| 7.2 |
| Elongation at Break, % | 7.0 to 35 | |
| 12 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 20 to 68 | |
| 200 to 260 |
| Shear Strength, MPa | 160 to 170 | |
| 1030 to 1330 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 300 | |
| 1720 to 2220 |
| Tensile Strength: Yield (Proof), MPa | 120 to 280 | |
| 1430 to 1850 |