90-silver 10-tin-oxide vs. ASTM A572 Steel
90-silver 10-tin-oxide belongs to the otherwise unclassified metals classification, while ASTM A572 steel belongs to the iron alloys. There are 6 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is 90-silver 10-tin-oxide and the bottom bar is ASTM A572 steel.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 77 to 82 | |
| 7.2 |
| Elongation at Break, % | 7.0 to 35 | |
| 18 to 25 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 20 to 68 | |
| 100 to 110 |
| Shear Strength, MPa | 160 to 170 | |
| 300 to 380 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 300 | |
| 470 to 620 |
| Tensile Strength: Yield (Proof), MPa | 120 to 280 | |
| 330 to 510 |