90-silver 10-tin-oxide vs. C66200 Brass
90-silver 10-tin-oxide belongs to the otherwise unclassified metals classification, while C66200 brass belongs to the copper alloys. There are 6 material properties with values for both materials. Properties with values for just one material (23, in this case) are not shown.
For each property being compared, the top bar is 90-silver 10-tin-oxide and the bottom bar is C66200 brass.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 77 to 82 | |
| 35 |
| Elongation at Break, % | 7.0 to 35 | |
| 8.0 to 15 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 20 to 68 | |
| 40 to 66 |
| Shear Strength, MPa | 160 to 170 | |
| 270 to 300 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 300 | |
| 450 to 520 |
| Tensile Strength: Yield (Proof), MPa | 120 to 280 | |
| 410 to 480 |