92-silver 8-tin-oxide vs. 3003 Aluminum
92-silver 8-tin-oxide belongs to the otherwise unclassified metals classification, while 3003 aluminum belongs to the aluminum alloys. There are 6 material properties with values for both materials. Properties with values for just one material (26, in this case) are not shown.
For each property being compared, the top bar is 92-silver 8-tin-oxide and the bottom bar is 3003 aluminum.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 76 to 80 | |
| 44 |
| Elongation at Break, % | 32 to 34 | |
| 1.1 to 28 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 62 to 110 | |
| 0.95 to 63 |
| Shear Strength, MPa | 150 to 210 | |
| 68 to 130 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 320 | |
| 110 to 240 |
| Tensile Strength: Yield (Proof), MPa | 120 to 300 | |
| 40 to 210 |