92-silver 8-tin-oxide vs. AISI 201L Stainless Steel
92-silver 8-tin-oxide belongs to the otherwise unclassified metals classification, while AISI 201L stainless steel belongs to the iron alloys. There are 6 material properties with values for both materials. Properties with values for just one material (27, in this case) are not shown.
For each property being compared, the top bar is 92-silver 8-tin-oxide and the bottom bar is AISI 201L stainless steel.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 76 to 80 | |
| 2.4 |
| Elongation at Break, % | 32 to 34 | |
| 22 to 46 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 62 to 110 | |
| 210 to 300 |
| Shear Strength, MPa | 150 to 210 | |
| 520 to 660 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 320 | |
| 740 to 1040 |
| Tensile Strength: Yield (Proof), MPa | 120 to 300 | |
| 290 to 790 |