92-silver 8-tin-oxide vs. AISI 305 Stainless Steel
92-silver 8-tin-oxide belongs to the otherwise unclassified metals classification, while AISI 305 stainless steel belongs to the iron alloys. There are 6 material properties with values for both materials. Properties with values for just one material (28, in this case) are not shown.
For each property being compared, the top bar is 92-silver 8-tin-oxide and the bottom bar is AISI 305 stainless steel.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 76 to 80 | |
| 2.4 |
| Elongation at Break, % | 32 to 34 | |
| 34 to 45 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 62 to 110 | |
| 200 to 210 |
| Shear Strength, MPa | 150 to 210 | |
| 400 to 470 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 320 | |
| 580 to 710 |
| Tensile Strength: Yield (Proof), MPa | 120 to 300 | |
| 230 to 350 |