92-silver 8-tin-oxide vs. AISI 440C Stainless Steel
92-silver 8-tin-oxide belongs to the otherwise unclassified metals classification, while AISI 440C stainless steel belongs to the iron alloys. There are 6 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is 92-silver 8-tin-oxide and the bottom bar is AISI 440C stainless steel.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 76 to 80 | |
| 2.4 |
| Elongation at Break, % | 32 to 34 | |
| 2.0 to 14 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 62 to 110 | |
| 39 to 88 |
| Shear Strength, MPa | 150 to 210 | |
| 430 to 1120 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 320 | |
| 710 to 1970 |
| Tensile Strength: Yield (Proof), MPa | 120 to 300 | |
| 450 to 1900 |