92-silver 8-tin-oxide vs. AZ91D Magnesium
92-silver 8-tin-oxide belongs to the otherwise unclassified metals classification, while AZ91D magnesium belongs to the magnesium alloys. There are 6 material properties with values for both materials. Properties with values for just one material (28, in this case) are not shown.
For each property being compared, the top bar is 92-silver 8-tin-oxide and the bottom bar is AZ91D magnesium.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 76 to 80 | |
| 11 |
| Elongation at Break, % | 32 to 34 | |
| 2.3 to 4.5 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 62 to 110 | |
| 4.2 to 7.7 |
| Shear Strength, MPa | 150 to 210 | |
| 120 to 140 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 320 | |
| 160 to 220 |
| Tensile Strength: Yield (Proof), MPa | 120 to 300 | |
| 80 to 130 |