92-silver 8-tin-oxide vs. Ductile Cast Iron
92-silver 8-tin-oxide belongs to the otherwise unclassified metals classification, while ductile cast iron belongs to the iron alloys. There are 6 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is 92-silver 8-tin-oxide and the bottom bar is ductile cast iron.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 76 to 80 | |
| 7.4 |
| Elongation at Break, % | 32 to 34 | |
| 2.1 to 20 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 62 to 110 | |
| 17 to 80 |
| Shear Strength, MPa | 150 to 210 | |
| 420 to 800 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 320 | |
| 460 to 920 |
| Tensile Strength: Yield (Proof), MPa | 120 to 300 | |
| 310 to 670 |