92-silver 8-tin-oxide vs. Grade 200 Maraging Steel
92-silver 8-tin-oxide belongs to the otherwise unclassified metals classification, while grade 200 maraging steel belongs to the iron alloys. There are 5 material properties with values for both materials. Properties with values for just one material (23, in this case) are not shown.
For each property being compared, the top bar is 92-silver 8-tin-oxide and the bottom bar is grade 200 maraging steel.
Metric UnitsUS Customary Units
Material Properties
| Elongation at Break, % | 32 to 34 | |
| 9.1 to 18 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 62 to 110 | |
| 140 to 160 |
| Shear Strength, MPa | 150 to 210 | |
| 600 to 890 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 320 | |
| 970 to 1500 |
| Tensile Strength: Yield (Proof), MPa | 120 to 300 | |
| 690 to 1490 |