92-silver 8-tin-oxide vs. Grade 250 Maraging Steel
92-silver 8-tin-oxide belongs to the otherwise unclassified metals classification, while grade 250 maraging steel belongs to the iron alloys. There are 5 material properties with values for both materials. Properties with values for just one material (22, in this case) are not shown.
For each property being compared, the top bar is 92-silver 8-tin-oxide and the bottom bar is grade 250 maraging steel.
Metric UnitsUS Customary Units
Material Properties
| Elongation at Break, % | 32 to 34 | |
| 7.3 to 17 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 62 to 110 | |
| 130 to 150 |
| Shear Strength, MPa | 150 to 210 | |
| 600 to 1060 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 320 | |
| 970 to 1800 |
| Tensile Strength: Yield (Proof), MPa | 120 to 300 | |
| 660 to 1740 |