92-silver 8-tin-oxide vs. Grade 300 Maraging Steel
92-silver 8-tin-oxide belongs to the otherwise unclassified metals classification, while grade 300 maraging steel belongs to the iron alloys. There are 5 material properties with values for both materials. Properties with values for just one material (22, in this case) are not shown.
For each property being compared, the top bar is 92-silver 8-tin-oxide and the bottom bar is grade 300 maraging steel.
Metric UnitsUS Customary Units
Material Properties
| Elongation at Break, % | 32 to 34 | |
| 6.5 to 18 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 62 to 110 | |
| 130 to 170 |
| Shear Strength, MPa | 150 to 210 | |
| 640 to 1190 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 320 | |
| 1030 to 2030 |
| Tensile Strength: Yield (Proof), MPa | 120 to 300 | |
| 760 to 1990 |