92-silver 8-tin-oxide vs. Grade 350 Maraging Steel
92-silver 8-tin-oxide belongs to the otherwise unclassified metals classification, while grade 350 maraging steel belongs to the iron alloys. There are 5 material properties with values for both materials. Properties with values for just one material (22, in this case) are not shown.
For each property being compared, the top bar is 92-silver 8-tin-oxide and the bottom bar is grade 350 maraging steel.
Metric UnitsUS Customary Units
Material Properties
| Elongation at Break, % | 32 to 34 | |
| 4.1 to 18 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 62 to 110 | |
| 98 to 190 |
| Shear Strength, MPa | 150 to 210 | |
| 710 to 1400 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 320 | |
| 1140 to 2420 |
| Tensile Strength: Yield (Proof), MPa | 120 to 300 | |
| 830 to 2300 |